长链烷氧基邻苯二甲腈的合成、表征及光谱性质研究

以3-硝基邻苯二甲腈、正己醇、正庚醇、十二醇、十八醇为主要原料,二甲亚砜为溶剂,在氢氧化锂的催化下发生亲核取代反应,合成了3-己/庚/十二/十八氧基邻苯二甲腈(α-nHexAPn/α-nHepAPn/α-nLAPn/α-nOAPn),通过正交试验获得最佳合成条件,采用1H-NMR及FT-IR对产物结构进行表征,测定了四种化合物的紫外及荧光光谱,探讨了烷氧基链长对产物紫外吸收及荧光光谱的影响.结果 表明:随着烷氧基链长的增加,取代邻苯二甲腈的紫外最大吸收波长基本不变,荧光最大发射波长发生蓝移.通过正交实验得知,当腈、醇及催化剂的摩尔比为2∶3∶3,反应时间72 h,产率为82.4％.     

高阶表面结构刚挠结合印制板制作技术

高阶表面结构刚挠结合印制电路板集合了混压设计,不对称设计等特点,且挠性板在外层,导致开窗处高度差较大,这一特点给制作增添了较大难度。本文选取此类典型刚挠结合板产品,分享部分关键制作技术。     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

One-step preparation of the superhydrophobic Al alloy surface with enhanced corrosion and wear resistance

Corrosion and wear failures are bottlenecks for restricting applications and developments of Al-based functional materials. As a new lubrication technology, superhydrophobic preparation provides an effective way to settle Al alloy corrosion. The preparation methods of superhydrophobic Al alloys are mainly multistep strategies. In this study, superhydrophobic Al alloy, has been prepared by an efficient one-step electrochemical etching process. Meanwhile, its micromorphology has been observed by a scanning electron microscope. The wettability has been measured by video optical contact angle meter. The corrosion behavior has been tested by electrochemical workstation, and wear performance has been characterized by friction tester. The results show that the micro-nanoterraced concave–convex structure has been fabricated and an as-prepared surface exhibits excellent superhydrophobic behavior. Further electrochemical and tribological tests show that corrosion resistance and wear resistance have also been significantly improved. This study provides a new method to prepare wear-resistant and corrosion-resistant Al alloy for widening applications of multifunctional Al-based engineering materials.     

Formation of SiC whiskers/leucite-based ceramic composites from low temperature hardening geopolymer

In this study, SiC whiskers (SCWS) reinforced geopolymer composites (SCWS/KGP) and their ceramic products (SCWS/leucite) were prepared, and effects of SiC whiskers contents on the microstructure and flexural strength of the SCWS/KGP and SCWS/leucite composites were investigated. The results show that the whisker addition has little influence on both phase composition and thermal shrinkage of the KGP composites, but a suitable content of whisker will result in the improved flexural strength, and when the SCWS content is 2 wt%, flexural strength of the SCWS/KGP composite is enhanced by 95% compared with the neat geopolymer. The flexural strength of the composites can be further enhanced significantly after the composites being treated at 1100 °C and 1200 °C and flexural strength of the composite with SCWS content of 2 wt% was 107% and 125% higher than the untreated counterpart, respectively. The increase in flexural strength of the composites should be attributed to the strong leucite formation, whisker debonding and pulling out from matrix during the fracturing process based on the good interfacial bonding state between whisker and leucite matrix.     

一种改进的特征匹配算法在碎片云测量建模中的应用

为满足超高速撞击典型Whipple防护构型的损伤评估需求,利用图像处理技术对碎片云序列阴影图像进行深入研究。使用超高速序列激光阴影成像仪得到三组不同实验条件下碎片云发展过程的高清阴影图像,分别对每组最具代表性的2帧进行图像处理分析;根据碎片云图像特点以及碎片运动特性,提出了一种改进的碎片二次特征匹配算法,该方法包含碎片粗定位、特征定义及初匹配和精确匹配三步策略;通过运用改进的匹配算法,对选取的相邻两帧图片完成碎片高效匹配,并提取匹配碎片的运动参数,进而分析碎片的速度分布和飞行角度分布,获取二次碎片云相关运动特性;得到三组实验各自的轨迹模拟图。根据得到的轨迹分析结果分别对三组实验的后板损伤进行估计,并通过与防护构型的实际损伤结果进行比较,验证了该方法的有效性。     

淀粉预糊化温度对肉粉肠品质特性的影响和机制研究

绿豆淀粉的预糊化是肉粉肠区别于其他熏煮香肠的关键加工工艺，因此，预糊化淀粉的温度对产品的品质至关重要。本研究将绿豆淀粉分别用75、85、95 ℃的热水进行预糊化后制备肉粉肠，探讨不同的预糊化温度对产品品质和淀粉糊化度（Degree of Starch Gelatinization，DSG）的影响。实验结果表明，随着预糊化淀粉温度的升高，肉粉肠的DSG和乳化稳定性显著增加（P<0.05），蒸煮损失显著降低（P<0.05），且大量自由水向不易流动水转变。同时，随预糊化淀粉温度的增加，肉粉肠的硬度、回复性、弹性、脆性、咀嚼性、致密性和亮度值（Lightness，L*）均显著增加（P<0.05），促进产品最终品质的形成。总体可接受评分在95 ℃的预糊化温度时达到最高（P<0.05）。此外，聚类分析（Hierarchical Cluster Analysis，HCA）结果表明，95 ℃的预糊化温度对肉粉肠的品质特性有上调的影响。综上所述，95 ℃是提高肉粉肠品质的最佳预糊化淀粉温度。     

Preparation,structure and microwave dielectric properties of novel La2MgGeO6 ceramics with hexagonal structure and adjustment of its τf value

A novel La₂MgGeO₆ ceramic was synthesized through a solid-state reaction process within a sintering temperature range of 1450–1550 °C. By a combination of X-ray diffraction and Rietveld refinement analyses, the ceramics were found to have a pure hexagonal phase structure belonging to space group R3/146. The scanning electron microscopy images revealed that the ceramic grains were closely connected. The effects of internal (lattice energy, valence bond, and fraction packing) and external factors (density) on the microwave properties of ceramics were also studied. The ceramic exhibited excellent microwave dielectric performances, with a relative permittivity (?_r) of 21.2, a quality factor (Q × f) of 52 360 GHz, and a temperature coefficient of resonant frequency (τ_f) of ?44.2 ppm/°C, when sintered at 1500 °C for 4 h. The τ_f value of the La₂MgGeO₆ ceramic doped with CaTiO₃ could be adjusted to zero. Particularly, 0.2La₂MgGeO₆-0.8CaTiO₃ ceramics have good microwave dielectric properties with τ_f = +2.1 ppm/°C, Q × f = 15 610 GHz, and ?_r = 40.3.     

Mesoporous Co–Mn Spinel Oxides as Efficient Catalysts for Low Temperature Propane Oxidation

Catalysis Letters - A series of mesoporous cobalt–manganese catalysts were successfully synthesized by sol–gel method as efficient catalysts for the propane oxidation. A significant...     

典型化工生产单元操作一体化实训室数字化课程学习系统建设

基于对典型化工生产单元操作一体化实训室数字化课程学习系统建设实践，将复杂且具有高度危险性的化工生产单元操作过程教学、培训等，构建成一个高度信息化的综合平台，利用视频、动画、微课、仿真等软硬件组成数字化的学习系统，即解决了学校资源、资金、场地、安全等的不足，方便学生随时随地学习，又解决了教师枯燥难教的困境，同时也解决了校内学资源碎片化、校际缺少共享等问题，为教学、培训、社会服务等提供便捷途径。